Can you refire a glazed piece




















I have heard of people firing the same piece up to 10 different times. Other times it is a deliberate plan. That many re-fires can start to weaken the clay, depending on the temperatures and the clay bodies used.

It gets a little more complicated with reduction firings, including Raku. If re-fired in an electric kiln, the black will burn out and you will get the clay color where it is bare.

Reduction and Raku glazes may or may not look good re-fired in oxidation, but they will probably look different. I took a workshop with Kevin Myers where we did Raku, followed by china painting on certain areas. We focused mainly on painting within the lines of crackle that had been created by the first firing.

Ceramics that you finished with sponge glazing is popular amongst Potters because it gives them the flexibility to create unique patterns and multilayer…. Pottery is an undeniably enjoyable but also challenging process. And along the way, one of the things that are bound to be recommended…. Underglazes and glazes are both common ways of adding color to a pottery piece.

Typically, both can be applied to pottery at different stages. This can make potters curious whether the two can be mixed together to save you from the hassle of adding multiple…. Glazing is a means to add colors to your pottery. It adds a touch of finesse to pottery pieces, giving them vibrant colors, eye-catching textures, and a smooth finish.

Another fun part of the pottery-making process and there are many ways to apply glazes, some…. Decorating pottery through spraying is very popular and relatively simple. Spray techniques are used on both clay and bisque to layer them with colors, textures, and slips. Transparent and colored glazes can also be applied using sprays.

Spray glazing is a learning process that requires…. Skip to content. Table of Contents. Post navigation Previous Previous. Next Continue. Similar Posts. Beginner Info Expand child menu Expand. Product Reviews Expand child menu Expand. Buyer Guides Expand child menu Expand.

Glazing Expand child menu Expand. Kiln Tips Expand child menu Expand. YouTube Pinterest. I have a problem that I never encountered.

A cone 5 fired bowl leaves a water mark on the table after it comes out of the dishwasher. The bottom of the pot feels dry and the glaze is a Miller glaze I've been using for years without any issues. The clay body is also Miller, Is this something that you recently made, or a piece you made a while ago? This may be way off base and too unprofessionial. I don't know if that is an option or not depends on what you are wanting. Good luck Kabe. Duncan French Dimensions need to be fired to at least cone So the low fire would not be sufficient.

If you want a low fire alternative without going the oven route which I personally don't like , you could use china paints or fired gold. They aren't raised but will get the job done. I'd do a test piece fired to Make sure you do your tests if possible with the same colors you will be putting it on top of as some colors act different when applied to already fired pieces. Here is my way of reglazing items. Please be aware I only work with ceramics and fire my glaze only 05 and Some problem items I take a bit of clear glaze and water it down and sort of use it with a sponge like rubbing compound to ruff it up surface just a bit to make new glaze stick.

Best method I prefer to use is warming it up in microwave however size is a factor as it has to be small enough to fit. Glaze crazing or glaze crackle is a network of lines or cracks in the fired glazed surface. It happens when a glaze is under tension. Generally, crazing is considered a glaze defect because the vessel can be significantly weaker than an uncrazed pot.

Craze lines can also harbor bacteria or germs. Fluid melt glazes, or those having high surface tension at melt stage, can blister on firing if applied too thick. Glazes having sufficient clay to produce excessive shrinkage on drying will crack and crawl during firing if applied too thick. Fluid melt glazes will run off ware if applied too thick. Can you Refire Raku? Typically, three coats are applied. Each dries slowly, hardening as it does so the glazes contain binders.